H150HF

特性/ Features

无卤Tg150±5℃℃,               Halogen-free Tg150±5℃℃

Dicy Cure,优秀的剥离强度           Dicy Cure ,Excellent peel strength  

优异耐热性 Td=358℃ T288=30min   Excellent thermal resistance Td=358℃ T288=30min          

Z轴热膨胀系数                  Low Z-CTE 3.5%

 

应用领域/ Applications 

手机、电脑、通讯设备、仪器仪表、摄像机、电视机等。

Mobile phone, Computer, Communication equipment , Instrumentation, VCR, Television, etc.

 

主要特性 / General properties

检测项目

Item               

单位

Unit

检测条件

Test Condition

规范值

Spec

典型值

Typical Value

玻璃化转变温度Tg

DSC

150±5

150.2

剥离强度  1oz                                                           Peel Strength

N/mm

288℃, 10S

≥1.05

1.52

热应力

Thermal   stress

S

288℃,solder   dip

10

180 s                         No   delamination

弯曲强度                                    Flexural   Strength

N/mm2

经向 LW

≥415

580

纬向CW

≥345

475

燃烧性

Flammability

E 24/125

UL94V-0

V-0

表面电阻Surface   Resistivity

After   moisture

≥1.0×104

5.21×107

体积电阻Volume   Resistivity

MΩ·cm

After   moisture

≥1.0×106

5.10×108

介电常数

Dielectric Constant

1 MHZ

C 24/23/50

≤5.4

4.6

介质损耗角正切

Loss Tangent

1 MHZ

C 24/23/50

≤0.035

0.015

耐电弧Arc   Resistance

S

 D48/50D0.5/23

≥60

120

击穿电压

Dielectric  Breakdown 

KV

 D48/50D0.5/23

≥40

57

吸水率Moisture   Absorption

%

D24/23

≤0.35

0.16

热分解温度Td

Weight Loss   5%

≥325

358

T288(不覆铜)

min

TMA

≥5

30

Z-CTE /50 -   260 ℃                             

%

TMA

≤4.0

3.5

相比漏电起痕指数 CTI                    

V

IEC-60112

175250

200

卤素含量

Halogen   content

Cl

ppm

 

EDX-GP

≤900

310

Br

ppm 

≤900

30

Cl+Br

ppm

≤1500

340

Specimen Thickness : 1.6mm ;    Specification sheetIPC-4101D/127is for your reference only

Explanation: C: Humidity conditioning;        D: Immersion conditioning in distilled water; 

           E: Temperature conditioning ;

 半固化片介绍-H150HFPP/ Prepreg instruction

H150HF PP UV Prepreg):

prepreg   type

Resin   Content(%)

压合厚度Cured thickness(mm/mil)

R/C(%)含量

公差Tolerance

Nominal

Range(±)mil

%

±

mm

mil

mm

mil

7628HRC

52

2

0.227

8.93

0.023

0.9

50

2

0.217

8.41

0.022

0.8

48

2

0.206

8.11

0.021

0.8

7628

45

2

0.192

7.56

0.019

0.8

43

2

0.183

7.20

0.018

0.7

1506

50

0

0.168

6.61

0.017

0.7

48

2

0.162

6.38

0.016

0.6

2116

59

2

0.135

5.31

0.014

0.5

57

2

0.130

5.12

0.013

0.5

55

2

0.123

4.84

0.012

0.5

53

2

0.117

4.61

0.011

0.5

1080

68

2

0.084

3.31

0.008

0.3

65

2

0.076

2.99

0.008

0.3

63

2

0.071

2.80

0.007

0.3

106

74

2

0.056

2.20

0.006

0.2

72

2

0.051

2.00

0.005

0.2

 

建议压制程式: Suggest cycle

 33d94835fd24d40c3241e6ae22792886.png


储存条件温度≤23℃、湿度≤50%,保存时间3个月;温度≤5℃、密封条件下,保存时间6个月.

Storage Condition: T≤23℃& ≤50%RH,Within 3 months;  T≤5 ℃ Within 6 months (seal condition).

在上述要求内,我司可立即安排PP送样;若有特殊要求,由供需双方商定。Follow above condition,

Our company will arrange sample immediately. We can discuss if you have special requirement.